Engineered Stiles Veneer Failure

7/18/14       
David R Sochar Member

Those of you that are concerned with such things may recall that I am a bit of a Luddite on the subject of engineered stiles for passage doors. Or "cost-accounted" stiles since that is, in my opinion, more important than the quality of the product. I have always made solid stiles and recommend same for others. Some folks disagree, and I am fine with that. It is a big world, and vive la diferance. What works is what works.

Well, I broke type and made some built up stiles for a pair of exterior Walnut doors recently. And today I get a call to come and see why the doors are 'falling apart".

I opted for 1/16" thick veneer for the faces, over ripped and glued top grade walnut for the cores. Since it is so hard to get decent looking wood, this seemed like a good time to go with the engineered/built up stiles (and rails),

We used powdered urea resin for the veneering. We have had a few bad experiences with Unibond 800 since it was reformulated, so were spooked by it. I wanted low/no water, but did not want to use epoxy since I felt the vacuum press would create too thin of a glue line. I swore off Urethane/Gorilla glue a few years ago, after learning it was not as good as other glues - even though I secretly loved it for veneering. The PUR was fresh and well mixed, temps were well over 70 degrees, etc. This all worked very well and the stiles and rails are were flawless.

Everything was tight and right. looking good and went to the finisher. Once complete, the carpenters set the doors and I went out to look at them for touch-up and look over the hardware and weatherstrip. We also used Tectus hinges and a corner silicone bead instead of the old standby- Q-lon. Nothing like keeping it interesting.

All was fine, except I noticed a fine crack along the grain - <1/32" wide and about 6" long, on a bottom rail, exterior face. I mentioned this to the finisher and he made it go away. These doors are finished as almost black, so the surface is about as hot as wood can get.

Now, 3 weeks later, the phone rings so I go out and find about 4-5 cracks in the stiles and the rails all about 12" long, less than 1/32" wide, in the grain of the veneer. The cracks are not above the joints in the core, just sort of near the center of the 5" rail and stile parts. All are on the exterior and more so on the lower third of the doors than just anywhere. The veneer is tight - not loose or peeling, but is very much open.

So.......where did we go wrong?

Wrong glue? That is what I'm thinking - it was the water in the powdered urea resin glue that readily went into the veneer and made it swell, then cure. Now, as the doors bake out in the Eastern exposure, the MC is decreasing and -c r a c k- the veneer splits. I did not take a MC reading during/after fabrication, so it may be pointless now, except as academic.

Meanwhile, I'm honing up my "Never a veneered door part again" speech and will stick to my guns. But currently I'm sick at the thought of how to fix this and what the future may hold. I also have been fantasizing about a job at McDonald's, where there is no risk, no stress.

7/18/14       #2: Engineered Stiles Veneer Failure ...
Mark Elliott Member

David,

I'm one of the engineered stile guys here.

I've always used epoxy, and though I never vac bagged, I've used cauls for pressing and never put that much pressure on that I worried about a starved surface.

The second thing is I've always used thicker shop sawn veneers for my faces. Always at least an 1/8" to 3/16" thick.

My staves were always close to being quarter sawn to minimize movement, that is I ripped them from flat sawn lumber, as I'm sure you probably did too.

So to answer your question, I think the veneers may have been too thin for an exterior door.

Sorry to hear about what happened and I hope this helps a little.

As an aside, I've never used an engineered core to save money. The added labor eats up any material savings quickly. What I've always liked about then when laid up with epoxy is they stay dead nuts flat and straight out of the cauls. The rigid glue line from the epoxy keeps them from ever bowing.

Regards,

Mark

7/18/14       #3: Engineered Stiles Veneer Failure ...
JeffD

I think David has probably forgotten more about door making than I know, but my little experience agrees with what Mark said. I build my doors in a similar way and it costs more to do them that if I were just to buy flat stock and mill. So no cost savings for me. I also re-saw my own skins and sand down to about 1/8" before gluing. I however only build interior doors so use TB3 and vac press for glue up.

I also wonder if the thin veneers are part of the problem? Walnut is pretty porous so I can definitely believe it would soak up plenty of moisture. Maybe this is a case of several small things combining to create a larger problem?

Anyway I hope you find a good way to resolve the situation. I know what you mean about "day job fantasizing" though, I'm now 6 weeks into my new shop and almost ready to start working for pay again!

good luck,
JeffD

7/18/14       #4: Engineered Stiles Veneer Failure ...
Larry Schweitzer Member

David has probably done many times the doors we have. I'm also an engineered core guy. Not to save $ but for the stability I hope it gives. I'm old fashioned and use resorcinol for exterior doors (but try to avoid them.) Great glue, no water but dark glue lines & slow. I also resaw faces and try to finish @ 1/8" thick. Vacuum bag with the parts inside of plastic sheeting because of the glue mess.

7/18/14       #5: Engineered Stiles Veneer Failure ...
Pat Gilbert

The main thing you did wrong was that you violated your own policy.

Then you tried something new and expected it to go off without a hitch.

7/19/14       #6: Engineered Stiles Veneer Failure ...
B.H. Davis Member

David,

I think your rails and stiles were doomed to split regardless of how thick the veneer. Nothing at all to do with how you made the doors but rather that very dark stain on a sun baked door made out of a not particularly stable wood species. I suspect that even solid rails and stiles would give you trouble in this installation scenario.

With regard to a McDonald's job I have a friend who was CEO of a pretty heavy duty company. Before he retired a few years ago he used to always say he wanted a job at the dollar store. All he would have to do is press the $1.00 key on the register all day !!

BH Davis

7/19/14       #8: Engineered Stiles Veneer Failure ...
Joe Calhoon

I would never do an exterior door with 1/16” veneer. Most of the door failures I have seen in the field from other companies are doors with veneer faces. I do not know what glue would be best for this application but probably nothing water based is good for thin veneer.

As many have said there is no cost savings for the small shop to build this way. The motive is to keep things straight. We always used solid stave cores butcher blocked to produce rift and quartered faces with 1/8” to 3/16” faces. See pictures. Ones on left are interior doors. For exterior we usually do a same species core.

This is nothing new. We have doors in our town built this way that are over 100 years old.
The weakness of this type of construction is the exposed glue line on cross rails. It will usually separate a little with exposure to weather. We normally use solid for the cross rails to avoid this. I do know a lot of east coast and other high exposure shops are having good luck with stave core thick veneers glued with epoxy. In dry Colorado we only use epoxy for building skis.

The only failure we had with this was a Sapelle door on a garage. We did the same doors on the house with no issues. The customer was parking her snow covered car with a overhead heater blowing across the car on to the door. Solid rails and panels cracked, And the 4mm thick veneer delaminated in several places. Part of the problem was the oil finish she requested offers no protection and we were not able to caulk the joints like we do with our water base finish. Anyway, we fixed the door and she stopped putting her car in wet.

My preferred method for exterior doors is 3 or 4 layer solid face glued with grain reversal. This way no exposed glue lines are to the weather and you get stability from the laminations. This only works on 2 ¼” and thicker doors and is more suitable for the Euro constructed doors we do.

Joe


View higher quality, full size image (1296 X 968)


View higher quality, full size image (1280 X 960)

7/19/14       #9: Engineered Stiles Veneer Failure ...
Gerry Brown

David,

The only glue failure I have encountered in 35 years of wood working was with plastic resin glue. I caught it before it went out the door and re-glued with titebond 3. I read a lot of theory on why the glue failed and in the end I thought it was due to over clamping a tight joint which resulted in a starved joint.

I think if you had followed the procedure you did with Titebond 2 or 3 you would be fine.

Hope you can sort it out but probably going to be a redo.

Gerry

7/19/14       #10: Engineered Stiles Veneer Failure ...
Charles Wright  Member

Website: http://www.northcreekwoodworks.com

Things that work:

*Liquid resin glue. Use heat to catalyze the glue.
*1/16 veneer should work
*Always cross band (1/16 min, 1/8 is better) Use poplar, aspen, basswood or maybe fir for core. I'm surprised no one mentioned this.
*Use strips of the face wood to cover the core wood at the edges.

7/21/14       #11: Engineered Stiles Veneer Failure ...
David R Sochar Member

Thanks for the good responses. Not that any of it is what I want to hear. I really feel dumb all of a sudden. Humbled may be a bit more charitable, tho no more accurate. I feel like I am in a confessional....

I knew about thicker -shop made veneer - since that is what we always use on this type of application. I did not cross band since it is all narrow parts - 5" at the most. I cross band when we need to stop all movement, especially in wide rails. I assumed the movement would be consistent with veneer and core all moving together. I like Gorilla glue for quick and simple veneer projects due to its lack of or low water content, but rejected it for this job.

I'm going to wait and see how much further things deteriorate. I am thinking we will have to rework the doors with 3/16" thick Walnut, both sides.

Here is the catch. There is always a catch. The glass in this project is a layered silk art glass that is made into an insulated panel. It's cost is about $8,000 all in, for 10 pcs of glass. We put glass in so it will not leak - silicone on both the exterior stops and the loose interior stops, so it is almost impossible to remove glass without breaking it. So we will have to bring the 200# doors back into the shop, route down the entire surface both sides, apply new veneer both sides, and then machine for hardware, then finish.

Oh yeah, did I mention Tectus hinges and Rocky Mountain custom hardware with a rabbeted strike plate?

Would you like fries with that?

7/21/14       #12: Engineered Stiles Veneer Failure ...
B.H. Davis  Member

Website: http://www.curvedmouldings.com

David,

That is a huge amount of work to fix the doors. I would strongly suggest taking the opportunity to do some test panels while you wait for any further possible deterioration to develop on the door.

With all the labor involved to remove and replace the veneer the last thing you want is another failure. I wouldn't just assume that the thicker veneer is going to solve the problem. A few test panels with various veneer thickness set out in the sun near the door would give you a good idea of what is going to happen.

Good luck with the repair.
BH Davis

7/21/14       #13: Engineered Stiles Veneer Failure ...
David R Sochar Member

Bernie -Thanks for the grounding. I do have a history of going off full speed ahead in the interest of getting something unpleasant behind me, causing yet more grief in the process.

A level head is always needed.

7/21/14       #14: Engineered Stiles Veneer Failure ...
B.H. Davis  Member

Website: http://www.curvedmouldings.com

"I do have a history of going off full speed ahead in the interest of getting something unpleasant behind me, causing yet more grief in the process."

Gee........sounds just like me. I need to learn to follow my own advice !

BH Davis

7/21/14       #15: Engineered Stiles Veneer Failure ...
Pat Gilbert

Looking at your website, you do nice work, way above the average.

When a person breaks his or the companies policy:

"I am a bit of a Luddite on the subject of engineered stiles."

"I have always made solid stiles and recommend same for others"

"I knew about thicker -shop made veneer"

"I assumed the movement would be consistent with veneer and core all moving together."

He:

"I really feel dumb all of a sudden. Humbled may be a bit more charitable, tho no more accurate. I feel like I am in a confessional...."

A person will always say to himself after an episode such as this, damn I knew I shouldn't have...

At least I always do...

7/21/14       #16: Engineered Stiles Veneer Failure ...
Larry

Dark finish & direct sun, ouch. Don't know that there is a perfect fix. Buy them some shade?

7/21/14       #17: Engineered Stiles Veneer Failure ...
Adam

David,

We have all been here at some point. You have our sympathies.

Obviously we are not looking at the doors. We have removed double insulated panes from doors without destroying them. They are very durable. The problem is glass actually scratches easier than one would think. That said I would take a couple of breaths before I dove into the veneer with a router.

Personally I would take the glass out and start over if at all feasible.

We have done a ton of vac bagging with epoxy. The thin line problem has never been a problem as long as both surfaces are abraded with 80 grit paper. This provides a decent width of glue line and plenty of surface area. Typically epoxy glue lines fail because of lack of abrasion and/or starvation from too much hand clamping force. The vac bag evenly distributes the clamping force and you would need to crank up the mercury to starve the joint.

Good luck

7/22/14       #18: Engineered Stiles Veneer Failure ...
ma

Had similar deal, customer used dark red paint. On a 100 degree day that panel measured 187 with our laser thermometer, a test of the white painted side in direct sun stayed right at ambient temp. It was so hot it re-liquefied the pitch in the vg fir and actually made the paint soft. Interesting enough the stiles and rails built engineered over fingerjoint staves stayed good other than a little pitch bleeding through.

7/28/14       #19: Engineered Stiles Veneer Failure ...
Gary

I would also check to see if the stiles with the cracks in them are cupped at all ? If cupping is substantial it will crack the veneer on the convex side. Under the extreme heat conditions it would not surprise me. I refuse to fabricate doors with a dark finish that are south facing and ,like you, I learned the hard way. That said there is always risk in the nature of our work and that is one reason we thrive on it. Go easy on your self; we are craftsman but we are not Gods. Dig deep and learn well from everything. Including the mistakes.

7/29/14       #20: Engineered Stiles Veneer Failure ...
Jim Lewis

I can't advise you on doors, Dave (and anyway you've gotten a ton of good advise already). But in addition to 80x sanding for epoxy, just throttle back your vacuum a bit for less pressure.

8/4/14       #21: Engineered Stiles Veneer Failure ...
Bill Member

Website: canadianacabinets.com

David, if you end up re veneering find a local shop with a cnc nester and let them mill the old veneer down. Safe and accurate.
They have spoil board cutters that will do a nice clean job.
Just a thought.
Bill

8/8/14       #22: Engineered Stiles Veneer Failure ...
roger watson

its gremlins, it could be combination of bad glue , ive used it I know, heat, veneer too thin/no cross banding, ive never had any faith in veneers where theres fluctuation in temp/humidity . I build my doors with solid wood and triple lamination on my stiles and rails in order to avoid warp . im not really a specialist in door manufacture so I keep it simple


Post a Response
  • Notify me of responses to this thread
  • Subscribe to email updates on this Forum
  • To receive email notification of additions to this forum thread,
    enter your name and email address, and then click the
    "Keep Me Posted" button below.

    Please Note: If you have posted a message or response,
    do not submit this request ... you are already signed up
    to receive notification!

    Your Name:
    E-Mail Address:
    Enter the correct numbers into the field below:
     

    Date of your Birth:



    Return to top of page

    Buy & Sell Exchanges | Forums | Galleries | Site Map

    FORUM GUIDELINES: Please review the guidelines below before posting at WOODWEB's Interactive Message Boards (return to top)

  • WOODWEB is a professional industrial woodworking site. Hobbyist and homeowner woodworking questions are inappropriate.
  • Messages should be kept reasonably short and on topic, relating to the focus of the forum. Responses should relate to the original question.
  • A valid email return address must be included with each message.
  • Advertising is inappropriate. The only exceptions are the Classified Ads Exchange, Machinery Exchange, Lumber Exchange, and Job Opportunities and Services Exchange. When posting listings in these areas, review the posting instructions carefully.
  • Subject lines may be edited for length and clarity.
  • "Cross posting" is not permitted. Choose the best forum for your question, and post your question at one forum only.
  • Messages requesting private responses will be removed - Forums are designed to provide information and assistance for all of our visitors. Private response requests are appropriate at WOODWEB's Exchanges and Job Opportunities and Services.
  • Messages that accuse businesses or individuals of alleged negative actions or behavior are inappropriate since WOODWEB is unable to verify or substantiate the claims.
  • Posts with the intent of soliciting answers to surveys are not appropriate. Contact WOODWEB for more information on initiating a survey.
  • Excessive forum participation by an individual upsets the balance of a healthy forum atmosphere. Individuals who excessively post responses containing marginal content will be considered repeat forum abusers.
  • Responses that initiate or support inappropriate and off-topic discussion of general politics detract from the professional woodworking focus of WOODWEB, and will be removed.
  • Participants are encouraged to use their real name when posting. Intentionally using another persons name is prohibited, and posts of this nature will be removed at WOODWEB's discretion.
  • Comments, questions, or criticisms regarding Forum policies should be directed to WOODWEB's Systems Administrator
    (return to top).

    Carefully review your message before clicking on the "Send Message" button - you will not be able to revise the message once it has been sent.

    You will be notified of responses to the message(s) you posted via email. Be sure to enter your email address correctly.

    WOODWEB's forums are a highly regarded resource for professional woodworkers. Messages and responses that are crafted in a professional and civil manner strengthen this resource. Messages that do not reflect a professional tone reduce the value of our forums.

    Messages are inappropriate when their content: is deemed libelous in nature or is based on rumor, fails to meet basic standards of decorum, contains blatant advertising or inappropriate emphasis on self promotion (return to top).

    Libel:   Posts which defame an individual or organization, or employ a tone which can be viewed as malicious in nature. Words, pictures, or cartoons which expose a person or organization to public hatred, shame, disgrace, or ridicule, or induce an ill opinion of a person or organization, are libelous.

    Improper Decorum:   Posts which are profane, inciting, disrespectful or uncivil in tone, or maliciously worded. This also includes the venting of unsubstantiated opinions. Such messages do little to illuminate a given topic, and often have the opposite effect. Constructive criticism is acceptable (return to top).

    Advertising:   The purpose of WOODWEB Forums is to provide answers, not an advertising venue. Companies participating in a Forum discussion should provide specific answers to posted questions. WOODWEB suggests that businesses include an appropriately crafted signature in order to identify their company. A well meaning post that seems to be on-topic but contains a product reference may do your business more harm than good in the Forum environment. Forum users may perceive your references to specific products as unsolicited advertising (spam) and consciously avoid your web site or services. A well-crafted signature is an appropriate way to advertise your services that will not offend potential customers. Signatures should be limited to 4-6 lines, and may contain information that identifies the type of business you're in, your URL and email address (return to top).

    Repeated Forum Abuse: Forum participants who repeatedly fail to follow WOODWEB's Forum Guidelines may encounter difficulty when attempting to post messages.

    There are often situations when the original message asks for opinions: "What is the best widget for my type of shop?". To a certain extent, the person posting the message is responsible for including specific questions within the message. An open ended question (like the one above) invites responses that may read as sales pitches. WOODWEB suggests that companies responding to such a question provide detailed and substantive replies rather than responses that read as a one-sided product promotion. It has been WOODWEB's experience that substantive responses are held in higher regard by our readers (return to top).

    The staff of WOODWEB assume no responsibility for the accuracy, content, or outcome of any posting transmitted at WOODWEB's Message Boards. Participants should undertake the use of machinery, materials and methods discussed at WOODWEB's Message Boards after considerate evaluation, and at their own risk. WOODWEB reserves the right to delete any messages it deems inappropriate. (return to top)


  • Forum Posting Help
    Your Name The name you enter in this field will be the name that appears with your post or response (return to form).
    Your Website Personal or business website links must point to the author's website. Inappropriate links will be removed without notice, and at WOODWEB's sole discretion. WOODWEB reserves the right to delete any messages with links it deems inappropriate. (return to form)
    E-Mail Address Your e-mail address will not be publicly viewable. Forum participants will be able to contact you using a contact link (included with your post) that is substituted for your actual address. You must include a valid email address in this field. (return to form)
    Subject Subject may be edited for length and clarity. Subject lines should provide an indication of the content of your post. (return to form)
    Thread Related Link and Image Guidelines Thread Related Links posted at WOODWEB's Forums and Exchanges should point to locations that provide supporting information for the topic being discussed in the current message thread. The purpose of WOODWEB Forums is to provide answers, not to serve as an advertising venue. A Thread Related Link that directs visitors to an area with inappropriate content will be removed. WOODWEB reserves the right to delete any messages with links or images it deems inappropriate. (return to form)
    Thread Related File Uploads Thread Related Files posted at WOODWEB's Forums and Exchanges should provide supporting information for the topic being discussed in the current message thread. Video Files: acceptable video formats are: .MOV .AVI .WMV .MPEG .MPG .MP4 (Image Upload Tips)   If you encounter any difficulty when uploading video files, E-mail WOODWEB for assistance. The purpose of WOODWEB Forums is to provide answers, not to serve as an advertising venue. A Thread Related File that contains inappropriate content will be removed, and uploaded files that are not directly related to the message thread will be removed. WOODWEB reserves the right to delete any messages with links, files, or images it deems inappropriate. (return to form)