Eliminating Micro-Bubbles in Polyurethane when Spraying with an AAA Gun

      A few tips on resolving a bubble problem in polyurethane finish when applying with an air-assisted airless spray setup. August 22, 2014

Question (WOODWEB Member)

Click to View Member Profile Member Contact Info Categories

I have been working on a finishing job using General Finishes clear satin polyurethane, running it through a Kremlin 10:14 with a CAT tip, 06-114. When using the product straight up with no thinning I had a huge amount of bubbles, almost like solvent pop, which did not level out and gave a very poor finish. I then added 5% of flow enhancer which did not seem to help at all. I thought it was the low humidity in the spray area. I then added 20% water to the mix and that solved the problem. I am thinking that due to the dry climate this winter the finish was skinning off too quickly and I was laying on the coats full 4 mils wet. I went to 2 mil wet and 2 extra coats and achieved a much better result. The pump was set to 35 fluid and 20 air. Hope these notes help someone else.

Forum Responses
(Finishing Forum)
From Contributor C:
With Air Assisted Airless systems like the Kremlin, micro bubbles can come from the piston action on the pump pulling the material through a small pick-up tube. The two changes that have helped people spraying the material with this type of equipment is to switch to a double orifice air cap and change to a larger diameter pick-up tube. This reduces the shearing effect of the product being forced through a small tube. The double orifice air cap breaks the product up into smaller droplets for better atomization.

From Contributor O:
I had a very similar problem with EM2000 sprayed out of a Kremlin 10-14 with MX gun and 06-096 tip. I tried an 09-096 tip but no real improvement. I searched around on the internet and found an old post on this forum where a member cured the problem by upping the fluid pressure to 50psi rather than dilute the finish. It worked.

From the original questioner

Click to View Member Profile Member Contact Info Categories

I upped the fluid pressure to 60 and that seemed to help a lot. I had it previously down at 30 with air up at 30. Thanks for the tips everyone.

Would you like to add information to this article?
Interested in writing or submitting an article?
Have a question about this article?

Have you reviewed the related Knowledge Base areas below?
  • KnowledgeBase: Knowledge Base

  • KnowledgeBase: Finishing

  • KnowledgeBase: Finishing: General Wood Finishing

    Would you like to add information to this article? ... Click Here

    If you have a question regarding a Knowledge Base article, your best chance at uncovering an answer is to search the entire Knowledge Base for related articles or to post your question at the appropriate WOODWEB Forum. Before posting your message, be sure to
    review our Forum Guidelines.

    Questions entered in the Knowledge Base Article comment form will not generate responses! A list of WOODWEB Forums can be found at WOODWEB's Site Map.

    When you post your question at the Forum, be sure to include references to the Knowledge Base article that inspired your question. The more information you provide with your question, the better your chances are of receiving responses.

    Return to beginning of article.

    Refer a Friend || Read This Important Information || Site Map || Privacy Policy || Site User Agreement

    Letters, questions or comments? E-Mail us and let us know what you think. Be sure to review our Frequently Asked Questions page.

    Contact us to discuss advertising or to report problems with this site.

    To report a problem, send an e-mail to our Webmaster

    Copyright © 1996-2019 - WOODWEB ® Inc.
    All rights reserved. No part of this publication may be reproduced in any manner without permission of the Editor.
    Review WOODWEB's Copyright Policy.

    The editors, writers, and staff at WOODWEB try to promote safe practices. What is safe for one woodworker under certain conditions may not be safe for others in different circumstances. Readers should undertake the use of materials and methods discussed at WOODWEB after considerate evaluation, and at their own risk.

    WOODWEB, Inc.
    335 Bedell Road
    Montrose, PA 18801

    Contact WOODWEB

  • WOODWEB - the leading resource for professional woodworkers

      Home » Knowledge Base » Knowledge Base Article