Glaze finish procedures

      Finishers share the steps they take with glaze finishes using conversion varnish. September 19, 2001

Our company does a lot of painted glazed finishes using conversion varnish. I'd be interested to see what different procedures all of you are using to apply catalyzed colored base coats, glazes and topcoats.

My process is as follows:

1. One coat catalyzed primer tinted to the base color shot on a good 4-5 mils thick.

2. We sand it completely smooth with as few burn-throughs as possible.

3. We tint the clear cv to the color we need using 866 tints at no more than 12 oz. per gallon. We thin about ten percent and up the catalyst an extra ounce per gallon. We also mix up clear cv and thin that about ten percent.

We then shoot the color out of a pressure pot about 5 mils thick. We spray color for about 20 minutes, then we go back to the first pieces and shoot them with clear with our airless-air assist. Doing this assures good adhesion and eliminates one sanding step. We let this set up overnight.

4. We then use scotch brite pads to scuff up the clearcoat going with the "grain", as the little scratches are slightly visible. Then we glaze and let it dry.

5. Finally a topcoat to lock it all in.

It's a long process that takes days, but the durability can't be beat especially in a kitchen or bath. If anybody has a better way I'd love to hear it.

Forum Responses
I see something that may bite you back in time and that is upping your catalyst by 1 ounce. No need to do this as you already are possibly adding up to 12 ounces to your resin. Always add catalyst based on untinted resin used, as the pigments are not crosslinkable.

Bob Niemeyer, forum technical advisor

1. Seal all rp door end grain and mdf edges with vinyl sealer.

2. Dust on a coat of catalyzed primer (usually just white) and scuff with 320.

3. Spray on another coat of primer and scuff with 400.

4. Tint glaze to desired color, thin and dust on with cup gun or pressure pot.

5. Wipe glaze with lint-free rags and let it flash off.

6. Mix up and spray on a toner to get the final desired color. (This step will 'soften' the look and allow you to even everything out. This may not be necessary if the look you want is achieved just with glaze).

7. Spray one or two coats of catalyzed clear coat.

* Use mdf wherever plywood is normally used (gables, fridge panels). Maple ply may seem smooth but the grain will affect the look of the glaze.

I'm concerned that I haven't been getting good adhesion with my topcoat, since we don't sand before glazing. It was my understanding that conversion varnish needed a scuffing before another coat, yet we've been laying down M.L. Campbell Resistant, glazing then spraying Krystal or Duravar. Is it possible that these clear coats are melting through the glaze AND the unscuffed CV?

Your M. L. Campbell finish schedule is wrong, even though it has worked for you so far. According to M. L. Campbell (assuming that your reducers and glazes are also the M. L. Campbell products), over your Resistant (this is their catalyzed pigmented conversion coating) you should lay down a coat of vinyl sealer. Then you apply your glaze coat and seal that in with another layer of vinyl sealer. Then you topcoat over that vinyl sealer with your Krystal or Duravar.

The idea is that the glaze is sandwiched between layers of vinyl sealer.

The total thickness of the dried film (Resistant, vinyl sealer coats, glaze and topcoats) should not exceed 5 dry mils. In that finish schedule you do not want to build more than 0.5 dry mils of vinyl sealer.

If you are laying down the topcoats soon after you have applied the Resistant, according to what you have described, then sure, it's likely that the solvents in your topcoat are strong enough to bite through the glaze coat, burn into the Resistant undercoat, locking the glaze into the topcoat.

The weak leak in your system is that enough time should have elapsed after you put on the glaze, manipulated it and allowed it to flash properly so that the undercoating of Resistant *should* require scuffing to insure good intercoat adhesion.

If you do a cross hatch adhesion test on one of your projects, that will tell you if you have committed acts of perfidy with your finish schedule. Even if everything is okay on your tests, sooner or later you could get bitten. Catalyzed finish systems are not known to be forgiving like lacquer finish systems are.

From the original questioner:
By scuffing our clearcoat with scotch brite pads we get enough scuff for the topcoat of cv to bite but not enough that the glaze hangs up in the scratchmarks. We have done crosshatch tests and the adhesion is excellent. Never assume the next coat of catalyzed finish will bite into the previous coat.

Would you like to add information to this article?
Interested in writing or submitting an article?
Have a question about this article?

Have you reviewed the related Knowledge Base areas below?
  • KnowledgeBase: Finishing

  • KnowledgeBase: Finishing: General Wood Finishing

  • KnowledgeBase: Knowledge Base

    Would you like to add information to this article? ... Click Here

    If you have a question regarding a Knowledge Base article, your best chance at uncovering an answer is to search the entire Knowledge Base for related articles or to post your question at the appropriate WOODWEB Forum. Before posting your message, be sure to
    review our Forum Guidelines.

    Questions entered in the Knowledge Base Article comment form will not generate responses! A list of WOODWEB Forums can be found at WOODWEB's Site Map.

    When you post your question at the Forum, be sure to include references to the Knowledge Base article that inspired your question. The more information you provide with your question, the better your chances are of receiving responses.

    Return to beginning of article.

    Refer a Friend || Read This Important Information || Site Map || Privacy Policy || Site User Agreement

    Letters, questions or comments? E-Mail us and let us know what you think. Be sure to review our Frequently Asked Questions page.

    Contact us to discuss advertising or to report problems with this site.

    To report a problem, send an e-mail to our Webmaster

    Copyright © 1996-2019 - WOODWEB ® Inc.
    All rights reserved. No part of this publication may be reproduced in any manner without permission of the Editor.
    Review WOODWEB's Copyright Policy.

    The editors, writers, and staff at WOODWEB try to promote safe practices. What is safe for one woodworker under certain conditions may not be safe for others in different circumstances. Readers should undertake the use of materials and methods discussed at WOODWEB after considerate evaluation, and at their own risk.

    WOODWEB, Inc.
    335 Bedell Road
    Montrose, PA 18801

    Contact WOODWEB

  • WOODWEB - the leading resource for professional woodworkers

      Home » Knowledge Base » Knowledge Base Article