Wood Strength Specs for Norway Spruce

      Looking for published engineering values for Norway Spruce. May 26, 2011

I'm trying to compare the strength specifications MOE/compression, etc. for Norway spruce (Picea abies) and Sitka spruce. I have the numbers for Sitka, but can't find them for Norway.

Forum Responses
(Furniture Making Forum)
From the original questioner:
I got a private response with these numbers: I've added PSI conversion units.

"Found these values at WolframAlpha.com searching Norway spruce as a material.
compressive yield strength | 30 MPa (megapascals) , 4351psi
flexural modulus | 9100 MPa (megapascals), 1,319,843 psi (moe)
wood indentation hardness | 1500 N (newtons)
modulus of rupture | 60 MPa (megapascals) 8702psi
shear strength | 5.3 MPa (megapascals), 768psi
tensile strength | 84 MPa (megapascals), 12183psi

toughness | 19.6 J (joules), 14.5 ftlb"

From Professor Gene Wengert, Sawing and Drying Forum technical advisor:
The mechanical properties for most commercial species are given in Table 4 in the link below. They give two values - green and 12% MC. They give one table with metric and the second table with English units. They have red, black, white, Engelmann and Sitka, but not Norway. I would expect Norway to fit within these values.

The numbers above at times seem far out for some properties, especially compression, tensile and MOR. The MOE above seems fairly low compared to other spruces. So, I wonder about the reliability of the quoted numbers.

Wood Handbook

Would you like to add information to this article?
Interested in writing or submitting an article?
Have a question about this article?

Have you reviewed the related Knowledge Base areas below?
  • KnowledgeBase: Knowledge Base

  • KnowledgeBase: Wood Engineering

  • KnowledgeBase: Wood Engineering: Wood Properties

    Would you like to add information to this article? ... Click Here

    If you have a question regarding a Knowledge Base article, your best chance at uncovering an answer is to search the entire Knowledge Base for related articles or to post your question at the appropriate WOODWEB Forum. Before posting your message, be sure to
    review our Forum Guidelines.

    Questions entered in the Knowledge Base Article comment form will not generate responses! A list of WOODWEB Forums can be found at WOODWEB's Site Map.

    When you post your question at the Forum, be sure to include references to the Knowledge Base article that inspired your question. The more information you provide with your question, the better your chances are of receiving responses.

    Return to beginning of article.

    Refer a Friend || Read This Important Information || Site Map || Privacy Policy || Site User Agreement

    Letters, questions or comments? E-Mail us and let us know what you think. Be sure to review our Frequently Asked Questions page.

    Contact us to discuss advertising or to report problems with this site.

    To report a problem, send an e-mail to our Webmaster

    Copyright © 1996-2021 - Woodweb.com
    All rights reserved. No part of this publication may be reproduced in any manner without permission of the Editor.
    Review Woodweb.com's Copyright Policy.

    The editors, writers, and staff at Woodweb.com try to promote safe practices. What is safe for one woodworker under certain conditions may not be safe for others in different circumstances. Readers should undertake the use of materials and methods discussed at Woodweb.com after considerate evaluation, and at their own risk.

    865 Troxel Road
    Lansdale, PA 19446

    Contact Us

  • WOODWEB - the leading resource for professional woodworkers

      Home » Knowledge Base » Knowledge Base Article